Jamplast JPPCABSI
丙烯腈丁二烯苯乙烯+聚碳酸酯
Jamplast, Inc.
Technical Data
產品說明
JPPCABSI engineering resin is designed to offer a balance of properties between impact strength, heat resistance and processability. It offers better processability than polycarbonate while offering high impact strength at both room and low temperatures compared to ABS. With a deflection temperature under load (264 psi, unannealed) of 230°F, JPPCABSI also offers high heat resistance compared to ABS. JPPCABSI engineering resin has been used in automotive instrument panel and interior trim applications.
總體
材料狀態 • 已商用：當前有效
供貨地區 • 北美洲
形式 • 顆粒料
加工方法 • 共擠出成型 • 片材擠出成型 • 注射成型
物理性能 額定值單位制 測試方法
比重 1.13g/cm³ ASTM D792
熔流率 (230°C/3.8 kg) 3.0g/10 min ASTM D1238
收縮率 - 流動 0.70% ASTM D955
吸水率 ASTM D570
23°C, 24 hr 0.15%
平衡, 23°C, 50% RH 0.32%
機械性能 額定值單位制 測試方法
抗張強度 2 ASTM D638
屈服 53.1MPa
斷裂 44.8MPa
伸長率 2 (斷裂) 130% ASTM D638
彎曲模量 2340MPa ASTM D790
彎曲強度 (屈服) 82.7MPa ASTM D790
沖擊性能 額定值單位制 測試方法
懸壁梁缺口沖擊強度 3 ASTM D256
-40°C, 3.18 mm 430J/m
-29°C, 3.18 mm 530J/m
23°C, 3.18 mm 730J/m
裝有測量儀表的落鏢沖擊 4 ASTM D3763
-29°C, 3.18 mm, Total Energy 62.1J
23°C, 3.18 mm, Total Energy 56.5J
硬度 額定值單位制 測試方法
洛氏硬度 (R 計秤) 115 ASTM D785
熱性能 額定值單位制 測試方法
熱變形溫度 ASTM D648
1.8 MPa, 未退火, 3.18 mm 110°C
1.8 MPa, 退火, 3.18 mm 121°C
線形膨脹系數 - 流動 (-40 到 82°C) 0.000074cm/cm/°C ASTM D696
備注
1 一般屬性：這些不能被視為規格。
2 類型 1, 51 mm/min
3 0.25 mm 缺口深度
4 3.39 m/sec
|